Comparing the enamel hardness by using mi varnish™ with recaldent™ before and after bracket bonding

Abstract

The objective of this study was to compare the hardness of enamel with and without MI Varnish (Recaldent) before and after bracket bonding. An experimental, quantitative, and longitudinal study was conducted, comprising 40 teeth in artificial saliva divided into four groups of ten each. The first group did not receive MI Varnish, while the second group did. Both groups were subjected to 500 thermal cycling cycles. A third group was treated without MI Varnish, and a fourth group with MI Varnish, both subjected to 1000 thermal cycling cycles. The Student's t-test was used. The results showed that after 500 cycles, the initial average hardness of the group without MI Varnish was 326.42 +/- 39.62 HV (kg/mm²), with a final average hardness of 226.42 +/- 35.18 HV (kg/mm²), meaning the enamel hardness decreased. The group with MI Varnish showed an initial average hardness of 310.28 +/- 41.13 HV (kg/mm²) and a final average hardness of 293.51 +/- 41.37 HV (kg/mm²). After 1000 cycles, the initial average hardness of the teeth without MI Varnish reached 307.98 +/- 39.62 HV (kg/mm²), and the final hardness was 230.33 +/- 47.83 HV (kg/mm²). The enamel hardness decreased more than after 500 cycles. The initial average hardness of the teeth with MI Varnish was 311.83 +/- 24.02 HV (kg/mm²), and the final hardness was 263.61 +/- 32.29 HV (kg/mm²). We concluded that after 500 cycles, the enamel hardness was greater with MI Varnish.

El objetivo del estudio fue compara la dureza del esmalte del esmalte con y sin MI Varnish (Recaldent) antes y después del pegado de bracket. Se realizó un estudio experimental, cuantitativo y longitudinal, comprende 40 dientes en saliva artificial divididos en cuatro grupos de diez cada uno. A un primer grupo no se le aplicó MI VARNISH, pero a un segundo grupo, sí. Ambos se sometieron a 500 ciclos de termociclado. Un tercer grupo fue tratado sin MI VARNISH y un cuarto grupo, con MI VARNISH , sometiéndose ambos a 1000 ciclos de termociclado. Se utilizó la prueba t de student. Los resultados fueron a 500 ciclos de termocilado la dureza inicial promedio del grupo sin MI VARNISH presentó 326.42 +/- 39.62 HV (kg/mm2 ) y una dureza final promedio de 226.42 +/-35.18 HV (kg/mm2 ), es decir, la dureza del esmalte disminuyó. El grupo con MI VARNISH reveló una dureza promedio inicial de 310.28 +/- 41.13 HV (kg/mm2 ) y una dureza promedio final de 293.51 +/- 41.37 HV (kg/mm2 ). A los 1000 ciclos, la dureza media inicial de las piezas sin MI VARNISH alcanzó 307.98 +/- 39.62 HV (kg/mm2 ); y la dureza final, 230.33 +/- 47.83 HV (kg/mm2 ). La dureza del esmalte disminuyó más que en 500 ciclos. La dureza media inicial de las piezas con MI VARNISH fue de 311.83 +/- 24.02 HV (kg/mm2 ) y una dureza final de 263.61 +/- 32.29 HV (kg/mm2 ). Llegamos a la conclusión que a los 500 ciclos la dureza del esmalte dental fue mayor con MI VARNISH.