Evaluation of the antibacterial capacity of two endodontic cements based on Calcium Hydroxide and Zinc Oxide against Enterococcus Faecalis strains. In vitro study.

Abstract

The objective of this study was to determine the antibacterial capacity of two endodontic cements based on calcium hydroxide and zinc oxide against Enterococcus Faecalis strains. In this in vitro, experimental, longitudinal, and prospective research, the sample consisted of 40 specimens divided into two experimental groups and two control groups. The agar diffusion test was used to determine the antibacterial capacity. For this, the Enterococcus Faecalis ATCC 29212 strain was inoculated onto Mueller Hinton agar plates, and four equidistant perforations were made where the materials were placed. The antibacterial capacity was evaluated by measuring the inhibition halos at 2, 24, and 48 hours. It was found that chlorhexidine gluconate produced the largest bacterial growth inhibition halos, which were statistically significant (p<0.05). When comparing the endodontic cements, it was found that the calcium hydroxide-based endodontic cement produced the largest bacterial growth inhibition halos, which were statistically significant compared to the zinc oxide-based endodontic cement (p<0.05). Conclusion: The calcium hydroxide-based endodontic cement demonstrated better antibacterial capacity against Enterococcus Faecalis.

El objetivo de este estudio fue determinar la capacidad antibacteriana de dos cementos endodónticos a base de hidróxido de calcio y óxido de zinc frente a cepas de Enterococcus Faecalis. En esta investigación in vitro, experimental, longitudinal y prospectivo la muestra estuvo constituida por 40 especímenes divididos en dos grupos experimentales y dos grupos controles. La prueba de difusión agar se utilizó para determinar la capacidad antibacteriana, para ello, en placas Petri con agar Mueller Hinton gelificado se inoculó la cepa de Enterococcus Faecalis ATCC 29212, se realizaron 4 perforaciones equidistantes donde se colocaron los materiales y la evaluación de la capacidad antibacteriana se realizó al medir los halos de inhibición a las 2, 24 y 48 horas. Se encontró que el gluconato de clorhexidina presentó los mayores halos de inhibición de crecimiento bacteriano que fueron estadísticamente significativos (p<0.05). Al comparar los cementos endodónticos, se encontró que el cemento endodóntico a base de hidróxido de calcio presentó los mayores halos de inhibición de crecimiento bacteriano que fueron estadísticamente significativos a diferencia del cemento endodóntico a base de óxido de zinc (p<0.05). En conclusión, el cemento endodóntico a base de hidróxido de calcio presentó mejor capacidad antibacteriana frente a Enterococcus Faecalis